![]() ![]() Abrading the surface will improve adhesion. ![]() Smooth surfaces should be cleaned with a suitable solvent or with soap and warm water to remove dirt and grease. MILLIPUT PUTTY 65203 FREEThe surfaces to which the putty is applied should be free from grease and dirt. Knead and roll in the hands for at least 5 minutes until the colours merge and become uniform and no streaks can be seen, and then mix for another minute. Mix together equal parts of each stick from the pack. It is very important when using this grade of Milliput, because the sticks are virtually the same colour, that you mix the two parts for at least five minutes. Sets under water and is electrically resistant.Also for cracks and chips in tiles, sinks and baths. For the repair of white domestic chinaware and for filling scores and dents in white domestic equipment e.g. I suggest experimenting with the amount, slowly adding more, until it behaves the way you want it to.Īlternatively, you can opt for using ProCreate Putty, which I saw mentioned here, and sounds like something that acts a bit more like you would expect of a watered down putty.White Milliput is a two part super fine white putty weighing 113g.įor the restoration of porcelain and other ceramics for the repair of antiques, objects d'art, Victorian dolls, picture mouldings, etc. The ratio really depends on what you want to achieve - what works best for your application. here: "I tried dilute Milliput and although it worked (sort of) it was messy and time consuming"). Note however, that some users complain about the manipulation of this mix (e.g. Here someone suggest adding a little soap with the water, as this will not only let it mix better, but also increase the drying time, although I think this might be detrimental for the structure. If what you need is a spreadable paste, start with an epoxy paste. If what you need is liquid epoxy, just start with that rather than adulterating epoxy putty. Epoxy-based products work best when used as manufactured start with a product of the right consistency for your needs. If your objective is just a surface coating or filler for minor defects, which doesn't need to be durable and won't be subject to a lot of handling, thinned Milliput may be adequate. The more water you add, the more it will degrade the result. ![]() Also, the moisture in the putty in contact with the surface it's applied to weakens the bond holding it in place. Smoothing the surface doesn't have a significant effect on the rest of the material.īut if you mix water into the putty, some of it will be trapped when the epoxy cures, which degrades and weakens the cured material. Water can be exploited to smooth the surface because it thins the filler and the epoxy doesn't stick when it or the surface is wet. The epoxy component doesn't mix with water, it's the filler that's affected. ![]() Some putties, like Milliput, will be softened by water while still uncured, but that's more of a side effect of the composition than a feature. The filler thickens it to give it the desired handling characteristics. The epoxy does the work of holding the mixture together and bonding it to the substrate. Epoxy putty, including Milliput, is a mixture of liquid epoxy and filler that makes the composite the consistency of clay. ![]()
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |